==Excimer Laser==

==Excimer Laser==

A Lambda Physik EMG 101 argon fluorine (ArF) excimer laser (shown in Figure 2) with an operating wavelength of 193 nm was used to ablate single-crystal CVD diamond. The laser is capable of delivering 120 mJ at a maximum repetition rate of 50 Hz and pulse duration of 20 nanoseconds. The pulse geometry is an asymmetrical flat top Gaussian with horizontal dimensions of 22 mm and vertical dimensions of 6 mm.

A Lambda Physik EMG 101 argon fluorine (ArF) excimer laser (shown in Figure 2) with an operating wavelength of 193 nm was used to ablate single-crystal CVD diamond. The laser is capable of delivering 120 mJ at a maximum repetition rate of 50 Hz and pulse duration of 20 nanoseconds. The pulse geometry is an asymmetrical flat top Gaussian with horizontal dimensions of 22 mm and vertical dimensions of 6 mm.

[[Image:Laser setup.jpg|center|300px|Figure 2: Image of Lambda Physik EMG 101 MSC excimer laser with cover removed.]]

[[Image:Laser setup.jpg|center|thumb|300px|Figure 2: Image of Lambda Physik EMG 101 MSC excimer laser with cover removed.]]

This particular laser shown in Figure 2 was over 30 years old when we first acquired it for the project. Much of my time (maybe too much :) ) has been spent restoring it so that it could maintain high energy levels for extended periods of time. All of my troubles are explicitly detailed in my logbooks which can be shared on request.

This particular laser shown in Figure 2 was over 30 years old when we first acquired it for the project. Much of my time (maybe too much :) ) has been spent restoring it so that it could maintain high energy levels for extended periods of time. All of my troubles are explicitly detailed in my logbooks which can be shared on request.

Figure 6 shows two columns of broad asymmetric patterns in a diamond sample cut using only a single lens for a varying number of laser pulses. Figure 7 shows the improvement in beam shape gained after using the three lens setup.

Figure 6 shows two columns of broad asymmetric patterns in a diamond sample cut using only a single lens for a varying number of laser pulses. Figure 7 shows the improvement in beam shape gained after using the three lens setup.

If the focal spot that created these patterns was rastered over an entire diamond it would result in a radiator with large surface variations rendering it unusable for GlueX. The focus of the laser defines the cutting tool with which the diamond is shaped. An ill-defined focused will ablate non-uniformly as the diamond is rastered across it making it extremely difficult to cut uniformly to 20 µm thickness without cracking the thin diamond membrane. The geometry of the focus also determines the fluence (laser energy per cm2 ) incident on the diamond surface. A tightly focused beam spot increases the available fluence, increasing the rate of ablation. It is therefore very important to measure the waist of the beam after L3 in the three lens system.

If the focal spot that created these patterns was rastered over an entire diamond it would result in a radiator with large surface variations rendering it unusable for GlueX. The focus of the laser defines the cutting tool with which the diamond is shaped. An ill-defined focused will ablate non-uniformly as the diamond is rastered across it making it extremely difficult to cut uniformly to 20 µm thickness without cracking the thin diamond membrane. The geometry of the focus also determines the fluence (laser energy per cm2 ) incident on the diamond surface. A tightly focused beam spot increases the available fluence, increasing the rate of ablation. It is therefore very important to measure the waist of the beam after L3 in the three lens system.